@article{oai:kutarr.kochi-tech.ac.jp:00000171,
 author = {Nishida, Ken and Honda, Yoshihisa and Yokoyama, Shintaro and Funakubo, Hiroshi and Yamamoto, Takashi and Saito, Keisuke and Katoda, Takashi},
 issue = {26},
 journal = {Applied Physics Letters},
 month = {Jun},
 note = {High-quality epitaxial La-substituted Pb (Zr0.65 Ti0.35) O3 films were grown on (100)c SrRu O3 ∥ (100)c SrTi O3 substrates at 600 °C using metal organic chemical vapor deposition. Single-phase perovskite was obtained for La (Pb+La) ratios ranging from 0 to 33%; La ions were selectively substituted at the Pb sites when the La (Pb+La) ratio was 6% or less and were substituted at both A and B sites when it was greater than 6%. Both the remanent polarization and coercive field monotonically decreased with the La (Pb+La) ratio, and the maximum field-induced strain was around 6%. This means that La substitution enhances the field-induced strain.},
 title = {Enhancement of field-induced strain by la substitution in epitaxial Pb (Zr,Ti) O3 films grown by metal organic chemical vapor deposition},
 volume = {90},
 year = {2007}
}